Effects of Pretreatment, Specimen Thickness, and Artificial Aging on Biaxial Flexural Strength of Two Types of Y-TZP Ceramics
Praktikertjänst AB.
Umeå universitet, Medicinska fakulteten, Institutionen för odontologi.
Umeå universitet, Medicinska fakulteten, Institutionen för odontologi.
2019 (Engelska)Ingår i: Operative dentistry, ISSN 0361-7734, E-ISSN 1559-2863, Vol. 44, nr 6, s. 615-624Artikel i tidskrift (Refereegranskat) Published
Abstract [en]

Objectives: To evaluate the effects of surface treatment, specimen thickness, and aging on the biaxial flexural strength (BFS) of two types of yttria-stabilized, tetragonal zirconia polycrystal (Y-TZP) ceramics.

Methods and Materials: Disc-shaped specimens, 0.4 and 1.3 mm thick, made from hot isostatic pressed (Denzir) and non–hot isostatic pressed (ZirPlus) Y-TZP, were sandblasted, heat treated, and autoclaved. The surface topography was assessed in accordance with European Standard 623-624:2004 and the BFS tests in accordance with International Organization for Standardization Standard 6872:2008. For statistical analyses, one-way Shapiro-Wilk test, analysis of variance (post hoc: least significant differences), Mann-Whitney U-test, and Pearson correlation tests (p<0.05) were used.

Results: As delivered, the BFS of the 0.4-mm ZirPlus was >1.3-mm ZirPlus (p<0.01), and the BFS of the 0.4-mm Denzir was >1.3-mm Denzir (p<0.001). Sandblasting with 0.2 MPa reduced the BFS of the ZirPlus and Denzir discs (p<0.01), whereas sandblasting with 0.6 MPa increased the BFS of the 0.4-mm Denzir (p<0.001) and reduced the BFS of the 0.4-mm ZirPlus (p<0.05). Heat treatment significantly reduced the BFS of all the groups except for the 0.6 MPa sandblasted 0.4-mm ZirPlus. Autoclaving reduced the BFS of the as-delivered ZirPlus and Denzir specimens (p<0.001), whereas autoclaving the 0.6 MPa sandblasted and heat-treated specimens had no effect (p>0.05) on the BFS. The 0.6 MPa sandblasted, heat-treated, and autoclaved 0.4-mm Denzir exhibited higher BFS than the 0.6 MPa sandblasted, heat-treated, and autoclaved 0.4-mm ZirPlus (p<0.05).

Conclusions: Thickness and surface treatment of Y-TZP–based ceramics should be considered since those factors could influence the BFS of the material.

Ort, förlag, år, upplaga, sidor
Operative Dentistry , 2019. Vol. 44, nr 6, s. 615-624
Nationell ämneskategori
Odontologi
Identifikatorer
URN: urn:nbn:se:umu:diva-158901DOI: 10.2341/18-071-LISI: 000496715600008PubMedID: 30978157Scopus ID: 2-s2.0-85074963737OAI: oai:DiVA.org:umu-158901DiVA, id: diva2:1315602
Tillgänglig från: 2019-05-14 Skapad: 2019-05-14 Senast uppdaterad: 2020-01-07Bibliografiskt granskad

Open Access i DiVA

Fulltext saknas i DiVA

Övriga länkar

Förlagets fulltextPubMedScopus

Person

Kou, WenSjögren, Göran

Sök vidare i DiVA

Av författaren/redaktören
Kou, WenSjögren, Göran
Av organisationen
Institutionen för odontologi
I samma tidskrift
Operative dentistry
Odontologi

Sök vidare utanför DiVA

GoogleGoogle Scholar

doi
pubmed
urn-nbn

Altmetricpoäng

doi
pubmed
urn-nbn
Totalt: 263 träffar
RefereraExporteraLänk till posten
Permanent länk

Direktlänk
Referera
Referensformat
  • apa
  • ieee
  • modern-language-association-8th-edition
  • vancouver
  • Annat format
Fler format
Språk
  • de-DE
  • en-GB
  • en-US
  • fi-FI
  • nn-NO
  • nn-NB
  • sv-SE
  • Annat språk
Fler språk
Utmatningsformat
  • html
  • text
  • asciidoc
  • rtf